LSAW/EFW Pipe
LSAW (Longitudinal double submerge arc welding) carbon steel pipe is a type of SAW pipe made of steel plates that were hot rolled by JCOE or UOE forming technology. JCOE technology represents the shaping and forming processes involved during manufacturing as well as the inner and outer welding and cold expansion carried out after welding.
LSAW pipe used to convey low pressure liquid or high pressure petroleum or natural gas, and can be also used widely in structural supports or foundation. The advantage for LSAW type is they could produce more thick wall thickness of pipes, maximum to 120mm.
Features:
-Large diameter steel pipes
-Thick walls
-High-Pressure resistance
-Low-temperature resistance
Tests:
-Chemical Component Analysis
-Mechanical Properties – Elongation, Yield Strength, Ultimate Tensile Strength
-Technical Properties – DWT Test, Impact Test, Blow Test, Flattening Test
-X-ray Test
-Exterior Size Inspection
-Hydrostatic Test
-UT Test
|
O.D. |
W.T. |
Length(m) |
|||||||
|
Inch |
mm |
Min.Yield Strength(Mpa) |
|||||||
|
Inch |
mm |
245(B) |
290(X42) |
360(X52) |
415(X60) |
450(X65) |
485(X70) |
555(X80) |
|
|
16 |
406 |
6.0-14.0 |
6.0-13.0 |
6.0-12.0 |
6.0-11.0 |
6.0-10.5 |
6.0-10.0 |
6.0-9.0 |
6.0-12.3 |
|
18 |
457 |
6.0-15.0 |
6.0-14.0 |
6.0-13.0 |
6.0-12.0 |
6.0-11.5 |
6.0-11.0 |
6.0-10.0 |
6.0-12.3 |
|
20 |
508 |
6.0-16.0 |
6.0-15.0 |
6.0-14.0 |
6.0-13.0 |
6.0-12.5 |
6.0-12.0 |
6.0-11.0 |
6.0-12.3 |
|
22 |
559 |
6.0-17.0 |
6.0-16.0 |
6.0-15.0 |
6.0-14.0 |
6.0-13.5 |
6.0-13.0 |
6.0-12.0 |
6.0-12.3 |
|
24 |
610 |
6.0-18.0 |
6.0-17.0 |
6.0-16.0 |
6.0-15.0 |
6.0-14.5 |
6.0-14.0 |
6.0-13.0 |
6.0-12.3 |
|
26 |
660 |
6.0-19.0 |
6.0-18.0 |
6.0-17.0 |
6.0-16.0 |
6.0-15.0 |
6.0-15.0 |
6.0-14.0 |
6.0-12.3 |
|
28 |
711 |
6.0-20.0 |
6.0-19.0 |
6.0-18.0 |
6.0-17.0 |
6.0-16.5 |
6.0-16.0 |
6.0-15.0 |
6.0-12.3 |
|
30 |
762 |
7.0-21.0 |
7.0-20.0 |
7.0-19.0 |
7.0-18.0 |
7.0-17.5 |
7.0-17.0 |
7.0-16.0 |
6.0-12.3 |
|
32 |
813 |
7.0-22.0 |
7.0-21.0 |
7.0-20.0 |
7.0-19.0 |
7.0-18.5 |
7.0-18.0 |
7.0-17.0 |
6.0-12.3 |
|
34 |
864 |
7.0-23.0 |
7.0-22.0 |
7.0-21.0 |
7.0-20.0 |
7.0-19.5 |
7.0-19.0 |
7.0-18.0 |
6.0-12.3 |
|
36 |
914 |
8.0-24.0 |
8.0-23.0 |
8.0-22.0 |
8.0-21.0 |
8.0-20.5 |
8.0-20.0 |
8.0-19.0 |
6.0-12.3 |
|
38 |
965 |
8.0-25.0 |
8.0-24.0 |
8.0-23.0 |
8.0-22.0 |
8.0-21.5 |
8.0-21.0 |
8.0-20.0 |
6.0-12.3 |
|
40 |
1016 |
8.0-26.0 |
8.0-25.0 |
8.0-24.0 |
8.0-23.0 |
8.0-22.5 |
8.0-22.0 |
8.0-21.0 |
6.0-12.3 |
|
42 |
1067 |
8.0-26.0 |
8.0-25.0 |
8.0-24.0 |
8.0-23.0 |
8.0-22.5 |
8.0-22.0 |
8.0-21.0 |
6.0-12.3 |
|
44 |
1118 |
9.0-27.0 |
9.0-26.0 |
9.0-24.5 |
9.0-23.5 |
9.0-22.8 |
9.0-22.0 |
9.0-21.0 |
6.0-12.3 |
|
46 |
1168 |
9.0-27.0 |
9.0-26.0 |
9.0-24.0 |
9.0-23.5 |
9.0-22.8 |
9.0-22.0 |
9.0-21.0 |
6.0-12.3 |
|
48 |
1219 |
9.0-28.0 |
9.0-27.0 |
9.0-25.4 |
9.0-24.0 |
9.0-23.5 |
9.0-23.0 |
9.0-22.0 |
6.0-12.3 |
|
52 |
1321 |
9.0-28.0 |
9.0-27.0 |
9.0-25.4 |
9.0-24.2 |
9.0-23.5 |
9.0-23.0 |
9.0-22.0 |
6.0-12.3 |
|
56 |
1422 |
10.0-29.0 |
10.0-28.0 |
10.0-26.0 |
10.0-24.5 |
10.0-23.8 |
10.0-23.0 |
10.0-22.0 |
6.0-12.3 |
|
60 |
1524 |
10.0-29.0 |
10.0-28.0 |
10.0-26.0 |
10.0-24.5 |
10.0-23.8 |
10.0-23.0 |
10.0-22.0 |
6.0-12.3 |
|
64 |
1626 |
10.0-30.0 |
10.0-29.0 |
10.0-27.0 |
10.0-25.4 |
10.0-24.8 |
10.0-24.0 |
10.0-23.0 |
6.0-12.3 |
|
68 |
1727 |
10.0-30.0 |
10.0-29.0 |
10.0-27.0 |
10.0-25.4 |
10.0-24.8 |
10.0-24.0 |
10.0-23.0 |
6.0-12.3 |
|
72 |
1829 |
10.0-30.0 |
10.0-29.0 |
10.0-27.0 |
10.0-25.4 |
10.0-24.8 |
10.0-24.0 |
10.0-23.0 |
6.0-12.3 |
Tolerance of Outside Diameter and Wall Thickness
|
Types |
Standard |
|||||
|
SY/T5040-2000 |
SY/T5037-2000 |
SY/T9711.1-1977 |
ASTM A252 |
AWWA C200-97 |
API 5L PSL1 |
|
|
Tube end OD deviation |
±0.5%D |
±0.5%D |
-0.79mm～+2.38mm |
<±0.1%T |
<±0.1%T |
±1.6mm |
|
Wall thickness |
±10.0%T |
D<508mm, ±12.5%T |
-8%T～+19.5%T |
<-12.5%T |
-8%T～+19.5%T |
5.0mm |
|
D>508mm, ±10.0%T |
T≥15.0mm, ±1.5mm |
|||||
机械
Chemical Composition and Mechanical Properties
|
Standard |
Grade |
Chemical Composition(max)% |
Mechanical Properties(min) |
|||||
|
C |
Mn |
Si |
S |
P |
Yield Strength(Mpa) |
Tensile Strength(Mpa) |
||
|
GB/T700-2006 |
A |
0.22 |
1.4 |
0.35 |
0.050 |
0.045 |
235 |
370 |
|
B |
0.2 |
1.4 |
0.35 |
0.045 |
0.045 |
235 |
370 |
|
|
C |
0.17 |
1.4 |
0.35 |
0.040 |
0.040 |
235 |
370 |
|
|
D |
0.17 |
1.4 |
0.35 |
0.035 |
0.035 |
235 |
370 |
|
|
GB/T1591-2009 |
A |
0.2 |
1.7 |
0.5 |
0.035 |
0.035 |
345 |
470 |
|
B |
0.2 |
1.7 |
0.5 |
0.030 |
0.030 |
345 |
470 |
|
|
C |
0.2 |
1.7 |
0.5 |
0.030 |
0.030 |
345 |
470 |
|
|
BS En10025 |
S235JR |
0.17 |
1.4 |
- |
0.035 |
0.035 |
235 |
360 |
|
S275JR |
0.21 |
1.5 |
- |
0.035 |
0.035 |
275 |
410 |
|
|
S355JR |
0.24 |
1.6 |
- |
0.035 |
0.035 |
355 |
470 |
|
|
DIN 17100 |
ST37-2 |
0.2 |
- |
- |
0.050 |
0.050 |
225 |
340 |
|
ST44-2 |
0.21 |
- |
- |
0.050 |
0.050 |
265 |
410 |
|
|
ST52-3 |
0.2 |
1.6 |
0.55 |
0.040 |
0.040 |
345 |
490 |
|
|
JIS G3101 |
SS400 |
- |
- |
- |
0.050 |
0.050 |
235 |
400 |
|
SS490 |
- |
- |
- |
0.050 |
0.050 |
275 |
490 |
|
|
API 5L PSL1 |
A |
0.22 |
0.9 |
- |
0.03 |
0.03 |
210 |
335 |
|
B |
0.26 |
1.2 |
- |
0.03 |
0.03 |
245 |
415 |
|
|
X42 |
0.26 |
1.3 |
- |
0.03 |
0.03 |
290 |
415 |
|
|
X46 |
0.26 |
1.4 |
- |
0.03 |
0.03 |
320 |
435 |
|
|
X52 |
0.26 |
1.4 |
- |
0.03 |
0.03 |
360 |
460 |
|
|
X56 |
0.26 |
1.1 |
- |
0.03 |
0.03 |
390 |
490 |
|
|
X60 |
0.26 |
1.4 |
- |
0.03 |
0.03 |
415 |
520 |
|
|
X65 |
0.26 |
1.45 |
- |
0.03 |
0.03 |
450 |
535 |
|
|
X70 |
0.26 |
1.65 |
- |
0.03 |
0.03 |
585 |
570 |
|
Katherine A. Fogg
Your email address will not be published. Required fields are marked with *
Their products are of excellent quality and they offer generous discounts. This is their third cooperation